Stainless Steel Wire
Alloys
California Fine Wire is a manufacturer of many types of Stainless Steel Wire. We supply the materials below in fine wire and ultra fine wire sizes.
Unit of Measure
Items |
100191 Stainless Steel 302 Wire List Price QUOTE
|
100192 Stainless Steel 304 Wire List Price QUOTE
|
100524 Stainless Steel 305 Wire List Price QUOTE
|
100193 Stainless Steel 308 Wire List Price QUOTE
|
100199 Stainless Steel 310 Wire List Price QUOTE
|
|||||
Brands | N/A California Fine Wire Co. | |||||||||
Specific Resistance | N/A 420.000 Ohm·cm/ft | N/A 420.000 Ohm·cm/ft | N/A 420.000 Ohm·cm/ft | N/A 455.000 Ohm·cm/ft | N/A 520.000 Ohm·cm/ft | |||||
Specific Resistivity | N/A 69.82 µOhm·cm²/cm | N/A 69.82 µOhm·cm²/cm | N/A 69.82 µOhm·cm²/cm | N/A 75.64 µOhm·cm²/cm | N/A 86.44 µOhm·cm²/cm | |||||
Commercial Resistance Tolerance (On Sizes below 0.020) | N/A 3.00 % | |||||||||
Temperature Coefficient of Resistance (0 to 100 Degree Celsius (ºC) Temperature) | N/A 0.00085 Ohm/Ohm/ºC | N/A 0.00085 Ohm/Ohm/ºC | N/A | N/A 0.000425 Ohm/Ohm/ºC | N/A | |||||
Thermal Electromotive Force (EMF) Vs Copper | N/A -0.014 | |||||||||
Density | N/A 7.92 g/cm³ | N/A 7.92 g/cm³ | N/A 7.92 g/cm³ | N/A 7.92 g/cm³ | N/A 7.97 g/cm³ | |||||
Youngs Modulus | N/A | N/A | N/A 29 x 106 psi | N/A | N/A 29 x 106 psi | |||||
Specific Heat at 20 Degree Celsius (ºC) Temperature | N/A 0.118 cal/g | N/A 0.118 cal/g | N/A 0.118 cal/g | N/A 0.180 cal/g | N/A 0.118 cal/g | |||||
Thermal Conductivity | N/A 1.903000 W/cm/ºC | N/A 0.19 W/cm/ºC | N/A 1.903000 W/cm/ºC | N/A 1.903000 W/cm/ºC | N/A 1.609000 W/cm/ºC | |||||
Coefficient of Linear Expansion | N/A 9.6 x 10-6 in/in ºC | N/A 9.6 x 10-6 in/in ºC | N/A 9.6 x 10-6 in/in ºC | N/A 9.6 x 10-6 in/in ºC | N/A 8.0 x 10-6 in/in ºC | |||||
Melting Point | N/A 1399.00 ºC | |||||||||
Industry Standards | N/A American Society for Testing and Materials (ASTM) A-313 American Society for Testing and Materials (ASTM) A-580 | N/A American Society for Testing and Materials (ASTM) A-313 American Society for Testing and Materials (ASTM) A-580 | N/A | N/A American Society for Testing and Materials (ASTM) A-580 | N/A American Society for Testing and Materials (ASTM) A-580 | |||||
Federal Specifications Standards and Test | N/A QQ-S-763 | N/A QQ-S-763 | N/A | N/A | N/A QQ-S-763 | |||||
Wire | N/A | |||||||||
Ribbon | N/A | |||||||||
Square | N/A | |||||||||
Insulated | N/A | |||||||||
Plated | N/A | |||||||||
Magnetic | N/A | |||||||||
Element | N/A Chromium (Cr) Iron (Fe) Manganese (Mn) | N/A Chromium (Cr) Iron (Fe) Manganese (Mn) Nickel (Ni) Silicon (Si) | N/A | N/A Chromium (Cr) Iron (Fe) Manganese (Mn) Nickel (Ni) Silicon (Si) | N/A Chromium (Cr) Iron (Fe) Manganese (Mn) Nickel (Ni) Silicon (Si) | |||||
Second Element | N/A Chromium (Cr) Iron (Fe) Manganese (Mn) | N/A Chromium (Cr) Iron (Fe) Manganese (Mn) Nickel (Ni) Silicon (Si) | N/A | N/A Chromium (Cr) Iron (Fe) Manganese (Mn) Nickel (Ni) Silicon (Si) | N/A Chromium (Cr) Iron (Fe) Manganese (Mn) Nickel (Ni) Silicon (Si) | |||||
Minimum Chromium (Cr) Composition | N/A 17.0000 % | N/A 18.0000 % | N/A | N/A 19.0000 % | N/A 24.0000 % | |||||
Maximum Chromium (Cr) Composition | N/A 19.0000 % | N/A 20.0000 % | N/A | N/A 21.0000 % | N/A 26.0000 % | |||||
Minimum Iron (Fe) Composition | N/A 68.0000 % | N/A 65.0000 % | N/A | N/A 64.0000 % | N/A 49.0000 % | |||||
Maximum Iron (Fe) Composition | N/A 75.0000 % | N/A 74.0000 % | N/A | N/A 71.0000 % | N/A 57.0000 % | |||||
Minimum Manganese (Mn) Composition | N/A | N/A | N/A | N/A 10.0000 % | N/A | |||||
Maximum Manganese (Mn) Composition | N/A 2.0000 % | N/A 2.0000 % | N/A | N/A 12.0000 % | N/A 2.0000 % | |||||
Minimum Nickel (Ni) Composition | N/A | N/A 8.0000 % | N/A | N/A 10.0000 % | N/A 19.0000 % | |||||
Maximum Nickel (Ni) Composition | N/A | N/A 12.0000 % | N/A | N/A 12.0000 % | N/A 22.0000 % | |||||
Maximum Silicone (Si) Composition | N/A | N/A 1.0000 % | N/A | N/A 1.0000 % | N/A 1.0000 % | |||||
Hard Ultimate Tensile Strength (UTS) | N/A 300000 psi | N/A 360000 psi | N/A 300000 psi | N/A 230000 psi | N/A 245000 psi | |||||
Annealed Ultimate Tensile Strength (UTS) | N/A 105000 psi | N/A 105000 psi | N/A 105000 psi | N/A 95000 psi | N/A 95000 psi | |||||
Hard Yield Tensile Strength (YTS) | N/A 280000 psi | N/A 280000 psi | N/A 280000 psi | N/A 205000 psi | N/A 230000 psi | |||||
Annealed Yield Tensile Strength (YTS) | N/A 45000 psi | N/A 45000 psi | N/A 45000 psi | N/A 35000 psi | N/A 35000 psi | |||||
Note | N/A All values may vary dependent on specific design and usage. | |||||||||
Operating Temperature | N/A 500.00 ºC | N/A 500.00 ºC | N/A | N/A | N/A | |||||
|