ELECTRICAL
- Specific Resistance (Ω–CM/F)
- 620.000
- Specific Resistivity (μ Ω–cm2/cm)
- 103.07
- Commercial Resistance Tolerance (On Sizes below .020)
- 3.00%
- Temperature Coefficient of Resistance (ohms/ohm/Deg. C {0 to 100°C})
- 0.00012
- Thermal EMF vs Copper
- -.014
PHYSICAL
- Density (gm/cm3)
- Density(lbs/in3)
- 0.30400
- Youngs Modulus (* 106 PSI)
- 31
- Specific Heat at 20 Deg C (cals/gm)
- 0.106
- Thermal Conductivity (watts/cm/Deg. C)
- 0.148000
- Coefficient of Linear Expansion (X 10-6 in/in Deg. C) Deg. C
- 7.4
- Melting Point °C
- 1354.00
- Melting Point °F
- 2470.00
SPECIFICATIONS
- ASTM
- ASTM B-166
- FEDERAL SPECS STANDARDS & TEST
- QQ-W-390
CAPABILITIES
- Wire
- YES
- Ribbon
- YES
- Square
- YES
- Insulated
- YES
- Plated
- YES
COMPOSITION
- ELEMENT
- Cr:
- MIN
- 14.0000
- NOMINAL
- 0.0000
- MAX
- 17.0000
- ELEMENT
- Fe:
- MIN
- 6.0000
- NOMINAL
- 0.0000
- MAX
- 10.0000
- ELEMENT
- Ni:
- MIN
- 0.0000
- NOMINAL
- 72.0000
- MAX
- 0.0000
TENSILE STRENGTH All values may vary dependent on specific design and usage
- UTS Hard:
- 200000
- UTS Stress Relieved:
- 0
- UTS Annealed:
- 80000
- YTS Tensile - Hard:
- 90000
- YTS Tensile - Stress Relieved:
- 0
- YTs Tensile - Annealed
- 30000
MISCELLANEOUS
- Magnetic
- None
- Operating Temp °C
- 0.00
- Operating Temp °F
- 0.00