Items |
100126 Molybdenum Wire List Price QUOTE
|
100809 Tantalum R05200 Wire List Price QUOTE
|
100220 Titanium 99% Wire List Price QUOTE
|
100211 Tungsten 99.95% CS Wire List Price QUOTE
|
||||
Brands | N/A California Fine Wire Co. | |||||||
Specific Resistance | N/A 31.000 Ohm·cm/ft | N/A 74.600 Ohm·cm/ft | N/A 252.000 Ohm·cm/ft | N/A 33.000 Ohm·cm/ft | ||||
Specific Resistivity | N/A 5.15 µOhm·cm²/cm | N/A 12.4 µOhm·cm²/cm | N/A 41.89 µOhm·cm²/cm | N/A 5.49 µOhm·cm²/cm | ||||
Commercial Resistance Tolerance (On Sizes below 0.020) | N/A 3.00 % | |||||||
Temperature Coefficient of Resistance (0 to 100 Degree Celsius (ºC) Temperature) | N/A 0.0033 Ohm/Ohm/ºC | N/A 0.0038 Ohm/Ohm/ºC | N/A 0.0034 Ohm/Ohm/ºC | N/A 0.0045 Ohm/Ohm/ºC | ||||
Thermal Electromotive Force (EMF) Vs Copper | N/A -0.014 | |||||||
Density | N/A 10.21 g/cm³ | N/A 16.61 g/cm³ | N/A 4.51 g/cm³ | N/A 19.29 g/cm³ | ||||
Specific Heat at 20 Degree Celsius (ºC) Temperature | N/A 0.064 cal/g | N/A 0.033 cal/g | N/A 0.082 cal/g | N/A 0.033 cal/g | ||||
Thermal Conductivity | N/A 1.397000 W/cm/ºC | N/A 0.594000 W/cm/ºC | N/A 0.15200 W/cm/ºC | N/A 1.274000 W/cm/ºC | ||||
Coefficient of Linear Expansion | N/A 5.4 x 10-6 in/in ºC | N/A 6.5 x 10-6 in/in ºC | N/A 8.5 x 10-6 in/in ºC | N/A 4.0 x 10-6 in/in ºC | ||||
Melting Point | N/A 2610.00 ºC | N/A 2890.00 ºC | N/A 1660.00 ºC | N/A 3420.00 ºC | ||||
Industry Standards | N/A | N/A American Society for Testing and Materials (ASTM) B-365 | N/A | N/A | ||||
Wire | N/A | |||||||
Ribbon | N/A | |||||||
Square | N/A | |||||||
Insulated | N/A | |||||||
Plated | N/A | |||||||
Element | N/A Molybdenum (Mo) | N/A Tantalum (Ta) | N/A Titanium (Ti) | N/A Tungsten (W) | ||||
Second Element | N/A Molybdenum (Mo) | N/A Tantalum (Ta) | N/A Titanium (Ti) | N/A Tungsten (W) | ||||
Minimum Molybdenum (Mo) Composition | N/A 99.9000 % | N/A | N/A | N/A | ||||
Minimum Tantalum (Ta) Composition | N/A | N/A 99.9600 % | N/A | N/A | ||||
Minimum Titanium (Ti) Composition | N/A | N/A | N/A 99.0000 % | N/A | ||||
Nominal Tungsten (W) Composition | N/A | N/A | N/A | N/A 99.9500 % | ||||
Hard Ultimate Tensile Strength (UTS) | N/A 320000 psi | N/A 100000 psi | N/A 90000 psi | N/A 600000 psi | ||||
Annealed Ultimate Tensile Strength (UTS) | N/A 100000 psi | N/A 50000 psi | N/A 75000 psi | N/A 250000 psi | ||||
Hard Yield Tensile Strength (YTS) | N/A 320000 psi | N/A | N/A | N/A | ||||
Annealed Yield Tensile Strength (YTS) | N/A 100000 psi | N/A | N/A | N/A | ||||
Note | N/A All values may vary dependent on specific design and usage. | |||||||
Magnetic | N/A | |||||||
Operating Temperature | N/A 200.00 ºC | N/A 500.00 ºC | N/A 500.00 ºC | N/A 150.00 ºC | ||||
|