| Items |
100068
Duranickel 301 Wire
List Price QUOTE
|
100125
Monel® 400 Wire
List Price QUOTE
|
100497
Monel® 404 Wire
List Price QUOTE
|
100137
Nickel 205 Wire
List Price QUOTE
|
100138
Nickel 211 Wire
List Price QUOTE
|
|
Brands
|
N/A
California Fine Wire Co.
|
|
Specific Resistance
|
N/A
255.000 Ohm·cm/ft
|
N/A
290.000 Ohm·cm/ft
|
N/A
319.000 Ohm·cm/ft
|
N/A
50.000 Ohm·cm/ft
|
N/A
102.00 Ohm·cm/ft
|
|
Specific Resistivity
|
N/A
42.39 µOhm·cm²/cm
|
N/A
48.21 µOhm·cm²/cm
|
N/A
53.03 µOhm·cm²/cm
|
N/A
8.30 µOhm·cm²/cm
|
N/A
16.96 µOhm·cm²/cm
|
|
Commercial Resistance Tolerance (On Sizes below 0.020)
|
N/A
3.00 %
|
|
Temperature Coefficient of Resistance (0 to 100 Degree Celsius (ºC) Temperature)
|
N/A
0.0006 Ohm/Ohm/ºC
|
N/A
0.0011 Ohm/Ohm/ºC
|
N/A
|
N/A
0.0048 Ohm/Ohm/ºC
|
N/A
0.0032 Ohm/Ohm/ºC
|
|
Thermal Electromotive Force (EMF) Vs Copper
|
N/A
-0.014
|
|
Density
|
N/A
8.89 g/cm³
|
N/A
8.83 g/cm³
|
N/A
8.89 g/cm³
|
N/A
8.89 g/cm³
|
N/A
8.72 g/cm³
|
|
Youngs Modulus
|
N/A
|
N/A
26 x 106 psi
|
N/A
|
N/A
|
N/A
|
|
Specific Heat at 20 Degree Celsius (ºC) Temperature
|
N/A
0.104 cal/g
|
N/A
0.127 cal/g
|
N/A
|
N/A
0.108 cal/g
|
N/A
|
|
Thermal Conductivity
|
N/A
0.238 W/cm/ºC
|
N/A
0.255000 W/cm/ºC
|
N/A
|
N/A
0.616000 W/cm/ºC
|
N/A
0.493000 W/cm/ºC
|
|
Coefficient of Linear Expansion
|
N/A
15.0 x 10-6 in/in ºC
|
N/A
7.70 x 10-6 in/in ºC
|
N/A
|
N/A
13.00 x 10-6 in/in ºC
|
N/A
|
|
Melting Point
|
N/A
1450.00 ºC
|
N/A
1350.00 ºC
|
N/A
1299.00 ºC
|
N/A
1450.00 ºC
|
N/A
1430.00 ºC
|
|
Industry Standards
|
N/A
|
N/A
American Society for Testing and Materials (ASTM) B-164
|
N/A
|
N/A
American Society for Testing and Materials (ASTM) B-267
|
N/A
American Society for Testing and Materials (ASTM) F-290
|
|
Federal Specifications Standards and Test
|
N/A
|
N/A
QQ-N-281
|
N/A
|
N/A
|
N/A
|
|
Wire
|
N/A
|
|
Ribbon
|
N/A
|
|
Square
|
N/A
|
|
Insulated
|
N/A
|
|
Plated
|
N/A
|
|
Element
|
N/A
Aluminum (Al) Nickel (Ni) Titanium (Ti)
|
N/A
Copper (Cu) Iron (Fe) Manganese (Mn) Nickel (Ni)
|
N/A
Copper (Cu) Nickel (Ni)
|
N/A
Nickel (Ni)
|
N/A
Manganese (Mn) Nickel (Ni)
|
|
Second Element
|
N/A
Aluminum (Al) Nickel (Ni) Titanium (Ti)
|
N/A
Copper (Cu) Iron (Fe) Manganese (Mn) Nickel (Ni)
|
N/A
Copper (Cu) Nickel (Ni)
|
N/A
Nickel (Ni)
|
N/A
Manganese (Mn) Nickel (Ni)
|
|
Minimum Aluminum (Al) Composition
|
N/A
4.0000 %
|
N/A
|
N/A
|
N/A
|
N/A
|
|
Maximum Aluminum (Al) Composition
|
N/A
4.7500 %
|
N/A
|
N/A
|
N/A
|
N/A
|
|
Minimum Copper (Cu) Composition
|
N/A
|
N/A
|
N/A
43.0000 %
|
N/A
|
N/A
|
|
Nominal Copper (Cu) Composition
|
N/A
|
N/A
32.5000 %
|
N/A
|
N/A
|
N/A
|
|
Maximum Copper (Cu) Composition
|
N/A
|
N/A
|
N/A
48.0000 %
|
N/A
|
N/A
|
|
Nominal Iron (Fe) Composition
|
N/A
|
N/A
2.5000 %
|
N/A
|
N/A
|
N/A
|
|
Maximum Iron (Fe) Composition
|
N/A
|
|
Nominal Manganese (Mn) Composition
|
N/A
|
N/A
2.0000 %
|
N/A
|
N/A
|
N/A
4.7500 %
|
|
Maximum Manganese (Mn) Composition
|
N/A
|
|
Minimum Nickel (Ni) Composition
|
N/A
|
N/A
|
N/A
52.0000 %
|
N/A
99.4500 %
|
N/A
|
|
Nominal Nickel (Ni) Composition
|
N/A
93.0000 %
|
N/A
63.0000 %
|
N/A
|
N/A
|
N/A
93.7000 %
|
|
Maximum Nickel (Ni) Composition
|
N/A
|
N/A
|
N/A
57.0000 %
|
N/A
|
N/A
|
|
Minimum Titanium (Ti) Composition
|
N/A
0.2500 %
|
N/A
|
N/A
|
N/A
|
N/A
|
|
Maximum Titanium (Ti) Composition
|
N/A
1.0000 %
|
N/A
|
N/A
|
N/A
|
N/A
|
|
Hard Ultimate Tensile Strength (UTS)
|
N/A
225000 psi
|
N/A
150000 psi
|
N/A
110000 psi
|
N/A
135000 psi
|
N/A
140000 psi
|
|
Annealed Ultimate Tensile Strength (UTS)
|
N/A
100000 psi
|
N/A
70000 psi
|
N/A
70000 psi
|
N/A
60000 psi
|
N/A
75000 psi
|
|
Hard Yield Tensile Strength (YTS)
|
N/A
|
N/A
125000 psi
|
N/A
100000 psi
|
N/A
|
N/A
|
|
Annealed Yield Tensile Strength (YTS)
|
N/A
|
N/A
30000 psi
|
N/A
25000 psi
|
N/A
|
N/A
|
|
Note
|
N/A
All values may vary dependent on specific design and usage.
|
|
Magnetic
|
N/A
|
|
Operating Temperature
|
N/A
|
N/A
815.00 ºC
|
N/A
|
N/A
1100.00 ºC
|
N/A
500.00 ºC
|