ELECTRICAL
- Specific Resistance (Ω–CM/F)
-
-
160.000
- Specific Resistivity (μ Ω–cm2/cm)
-
-
26.6
- Commercial Resistance Tolerance (On Sizes below .020)
-
-
3.00%
- Temperature Coefficient of Resistance (ohms/ohm/Deg. C {0 to 100°C})
-
-
0
- Thermal EMF vs Copper
-
-
-.014
PHYSICAL
- Density (gm/cm3)
- Density(lbs/in3)
-
-
0.32300
- Youngs Modulus (* 106 PSI)
-
-
20
- Specific Heat at 20 Deg C (cals/gm)
-
-
0.090
- Thermal Conductivity (watts/cm/Deg. C)
-
-
0.369000
- Coefficient of Linear Expansion (X 10-6 in/in Deg. C) Deg. C
-
-
16.4
- Melting Point °C
-
-
1150.00
- Melting Point °F
-
-
2100.00
SPECIFICATIONS
- ASTM
-
-
ASTM B-206
- FEDERAL SPECS STANDARDS & TEST
-
-
QQ-W-321
CAPABILITIES
- Wire
-
-
YES
- Ribbon
-
-
YES
- Square
-
-
YES
- Insulated
-
-
YES
- Plated
-
-
YES
COMPOSITION
- ELEMENT
-
-
Cu:
- MIN
-
-
0.0000
- NOMINAL
-
-
79.0000
- MAX
-
-
0.0000
- ELEMENT
-
-
Ni:
- MIN
-
-
0.0000
- NOMINAL
-
-
21.0000
- MAX
-
-
0.0000
TENSILE STRENGTH
All values may vary dependent on specific design and usage
- UTS Hard:
-
-
75000
- UTS Stress Relieved:
-
-
0
- UTS Annealed:
-
-
53000
- YTS Tensile - Hard:
-
-
70000
- YTS Tensile - Stress Relieved:
-
-
0
- YTs Tensile - Annealed
-
-
16000
MISCELLANEOUS
- Magnetic
-
-
None
- Operating Temp °C
-
-
0.00
- Operating Temp °F
-
-
0.00