ELECTRICAL
- Specific Resistance (Ω–CM/F)
-
-
520.000
- Specific Resistivity (μ Ω–cm2/cm)
-
-
86.44
- Commercial Resistance Tolerance (On Sizes below .020)
-
-
3.00%
- Temperature Coefficient of Resistance (ohms/ohm/Deg. C {0 to 100°C})
-
-
0
- Thermal EMF vs Copper
-
-
-.014
PHYSICAL
- Density (gm/cm3)
- Density(lbs/in3)
-
-
0.28800
- Youngs Modulus (* 106 PSI)
-
-
29
- Specific Heat at 20 Deg C (cals/gm)
-
-
0.118
- Thermal Conductivity (watts/cm/Deg. C)
-
-
1.609000
- Coefficient of Linear Expansion (X 10-6 in/in Deg. C) Deg. C
-
-
8.0
- Melting Point °C
-
-
1399.00
- Melting Point °F
-
-
2550.00
SPECIFICATIONS
- ASTM
-
-
ASTM A-580
- FEDERAL SPECS STANDARDS & TEST
-
-
QQ-S-763
CAPABILITIES
COMPOSITION
- Wire
-
-
YES
- Ribbon
-
-
YES
- Square
-
-
YES
- Insulated
-
-
YES
- Plated
-
-
YES
- ELEMENT
-
-
Cr:
- MIN
-
-
24.0000
- NOMINAL
-
-
0.0000
- MAX
-
-
26.0000
- ELEMENT
-
-
Fe:
- MIN
-
-
49.0000
- NOMINAL
-
-
0.0000
- MAX
-
-
57.0000
- ELEMENT
-
-
Mn:
- MIN
-
-
0.0000
- NOMINAL
-
-
0.0000
- MAX
-
-
2.0000
- ELEMENT
-
-
Ni:
- MIN
-
-
19.0000
- NOMINAL
-
-
0.0000
- MAX
-
-
22.0000
- ELEMENT
-
-
Si:
- MIN
-
-
0.0000
- NOMINAL
-
-
0.0000
- MAX
-
-
1.0000
TENSILE STRENGTH
Note: All values may vary dependent on specific design and usage
- UTS Hard:
-
-
245000
- UTS Stress Relieved:
-
-
0
- UTS Annealed:
-
-
95000
- YTS Tensile - Hard:
-
-
230000
- YTS Tensile - Stress Relieved:
-
-
0
- YTs Tensile - Annealed
-
-
35000
MISCELLANEOUS
- Magnetic
-
-
None
- Operating Temp °C
-
-
0.00
- Operating Temp °F
-
-
0.00