ELECTRICAL
- Specific Resistance (Ω–CM/F)
-
-
455.000
- Specific Resistivity (μ Ω–cm2/cm)
-
-
75.64
- Commercial Resistance Tolerance (On Sizes below .020)
-
-
3.00%
- Temperature Coefficient of Resistance (ohms/ohm/Deg. C {0 to 100°C})
-
-
0.000425
- Thermal EMF vs Copper
-
-
-.014
PHYSICAL
- Density (gm/cm3)
- Density(lbs/in3)
-
-
0.28600
- Youngs Modulus (* 106 PSI)
-
-
0
- Specific Heat at 20 Deg C (cals/gm)
-
-
0.180
- Thermal Conductivity (watts/cm/Deg. C)
-
-
1.903000
- Coefficient of Linear Expansion (X 10-6 in/in Deg. C) Deg. C
-
-
9.6
- Melting Point °C
-
-
1399.00
- Melting Point °F
-
-
2550.00
SPECIFICATIONS
- ASTM
-
-
ASTM A-580
CAPABILITIES
- Wire
-
-
YES
- Ribbon
-
-
YES
- Ribbon
-
-
YES
- Insulated
-
-
YES
- Plated
-
-
YES
COMPOSITION
- ELEMENT
-
-
Cr:
- MIN
-
-
19.0000
- NOMINAL
-
-
0.0000
- MAX
-
-
21.0000
- ELEMENT
-
-
Fe:
- ELEMENT
-
-
64.0000
- NOMINAL
-
-
0.0000
- MAX
-
-
71.0000
- ELEMENT
-
-
Mn:
- ELEMENT
-
-
10.0000
- NOMINAL
-
-
0.0000
- MAX
-
-
12.0000
- ELEMENT
-
-
Ni:
- NOMINAL
-
-
10.0000
- NOMINAL
-
-
0.0000
- MAX
-
-
12.0000
- ELEMENT
-
-
Si:
- NOMINAL
-
-
0.0000
- NOMINAL
-
-
0.0000
- MAX
-
-
1.0000
TENSILE STRENGTH
All values may vary dependent on specific design and usage
- UTS Hard:
-
-
230000
- UTS Stress Relieved:
-
-
0
- UTS Annealed:
-
-
95000
- YTS Tensile - Hard:
-
-
205000
- YTS Tensile - Stress Relieved:
-
-
0
- YTs Tensile - Annealed
-
-
35000
MISCELLANEOUS
- Magnetic
-
-
None
- Operating Temp °C
-
-
0.00
- Operating Temp °F
-
-
0.00