California Fine Wire is a manufacturer of Inconel® X750 fine wire. Our specialty is supplying Inconel® X750 wire in the smallest diameters on the market.
Unit of Measure

Specifications

Brands

N/A California Fine Wire Co.

Industry Standards

N/A Aerospace Material Specifications (AMS) 5698

Second Element

N/A Chromium (Cr) Manganese (Mn) Nickel (Ni) Niobium (Nb) Tantalum (Ta) Titanium (Ti)

Electrical

Specific Resistivity

N/A 121.52 µOhm·cm²/cm

Commercial Resistance Tolerance (On Sizes below 0.020)

N/A 3.00 %

Thermal Electromotive Force (EMF) Vs Copper

N/A -0.014

Specific Resistance

N/A 731.000 Ohm·cm/ft

Physical

Density

N/A 8.25 g/cm³

Youngs Modulus

N/A 31 x 106 psi

Specific Heat at 20 Degree Celsius (ºC) Temperature

N/A 0.103 cal/g

Thermal Conductivity

N/A 0.120000 W/cm/ºC

Coefficient of Linear Expansion

N/A 7.0 x 10-6 in/in ºC

Melting Point

N/A 816.00 ºC

Composition

Element

N/A Chromium (Cr) Manganese (Mn) Nickel (Ni) Niobium (Nb) Tantalum (Ta) Titanium (Ti)

Nominal Nickel (Ni) Composition

N/A 70.0000 %

Minimum Chromium (Cr) Composition

N/A 14.0000 %

Maximum Chromium (Cr) Composition

N/A 17.0000 %

Minimum Titanium (Ti) Composition

N/A 2.2500 %

Maximum Titanium (Ti) Composition

N/A 2.7500 %

Maximum Manganese (Mn) Composition

N/A 1.0000 %

Maximum Niobium (Nb) Composition

N/A 1.2000 %

Maximum Tantalum (Ta) Composition

N/A 1.2000 %

Tensile Strength

Hard Ultimate Tensile Strength (UTS)

N/A 220000 psi

Annealed Ultimate Tensile Strength (UTS)

N/A 130000 psi

Hard Yield Tensile Strength (YTS)

N/A 150000 psi

Annealed Yield Tensile Strength (YTS)

N/A 105000 psi

Note

N/A All values may vary dependent on specific design and usage.