ELECTRICAL
- Specific Resistance (Ω–CM/F)
- 25.000
- Specific Resistivity (μ Ω–cm2/cm)
- 4.16
- Commercial Resistance Tolerance (On Sizes below .020)
- 3.00%
- Temperature Coefficient of Resistance (ohms/ohm/Deg. C {0 to 100°C})
- 0
- Thermal EMF vs Copper
- -.014
PHYSICAL
- Density (gm/cm3)
- Density (gm/cm3)
- 0.09700
- Youngs Modulus (* 106 PSI)
- 0
- Specific Heat at 20 Deg C (cals/gm)
- 0.230
- Thermal Conductivity (watts/cm/Deg. C)
- 0.000000
- Coefficient of Linear Expansion (X 10-6 in/in Deg. C) Deg. C
- 22.1
- Melting Point °C
- 632.00
- Melting Point °F
- 1170.00
SPECIFICATIONS
- ASTM
- ASTM B-211
- ASTM
- ASTM B-221
CAPABILITIES
- Wire
- YES
- Ribbon
- YES
- Square
- YES
- Insulated
- YES
- Plated
- YES
COMPOSITION
- ELEMENT
- Al:
- MIN
- 0.0000
- NOMINAL
- 94.7500
- MAX
- 0.0000
- ELEMENT
- Si:
- MIN
- 0.0000
- NOMINAL
- 5.2500
- MAX
- 0.0000
TENSILE STRENGTH Note: All values may vary dependent on specific design and usage
- UTS Hard:
- 41000
- UTS Stress Relieved:
- 0
- UTS Annealed:
- 19000
- YTS Tensile - Hard:
- 39000
- YTS Tensile - Stress Relieved:
- 0
- YTs Tensile - Annealed
- 7000
MISCELLANEOUS
- Magnetic
- None
- Operating Temp °C
- 0.00
- Operating Temp °F
- 0.00